Grade | Raw polymer Hardness ° A |
Spec. Gravity | Expected Mooney ML1+@100 °C |
ACN Content | Exra. % | Poly Ratio | Remarks |
RA - 70 | 50 ± 5 | 1.04 ± 0.02 | 50 ± 5 | 33% | 9 | 70 / 30 | 70 / 30 Blend, 50 MV |
RA - 7060 | 55 ± 5 | 1.04 ± 0.02 | 60 ± 5 | 33% | 9 | 70 / 30 | 70/30 Blend, 60 MV |
RA - 7047 | 50 ± 5 | 1.06 ± 0.02 | 55 ± 5 | 33% | 18 | 70 / 30 | General Purpose |
RA - 703G | 60 ± 5 | 1.04 ± 0.02 | 75 ± 5 | 33% | 5 | 70 / 30 | 70/30 blend, 75 MV |
RA - 7573 | 50 ± 5 | 1.02 ± 0.2 | 65 ± 5 | 33% | 11.75 | 70 / 30 | General Purpose |
RA - 7360 | 60 ± 5 | 1.04 ± 0.02 | 65 ± 5 | 33% | 1 | 70 / 30 | 70/30 Blend, High Tensile |
RA - 7380 | 60 ± 5 | 1.04 ± 0.02 | 80 ± 5 | 33% | 1 | 70 / 30 | High Mooney, High Tensile |
RA - L 7360 | 60 ± 5 | 1.04 ± 0.02 | 65 ± 5 | 28% | 1 | 70 / 30 | 70/30 Blend, Low Temp. Resistance |
RA - 75 | 65 ± 5 | 1.06 ± 0.02 | 70 ± 5 | 39% | 8 | 70 / 30 | 70/30 Blend, High A.C.N. |
RA - 4465 | 60 ± 5 | 1.03 ± 0.02 | 60± 5 | 44% | 1 | 70 / 30 | Ultra High ACN Content for Very High Oil and Fuel Resistance |
RA - 6040 | 65 ± 5 | 1.11 ± 0.02 | 90± 5 | 33% | 2.4 | 60 / 40 | 60/40 Blend for High Ozone Resistance |
RA - 6490 | 65 ± 5 | 1.07 ± 0.02 | 90± 5 | 44% | 1 | 60 / 40 | For high oil/fuel resistance & low shrinkage |
NBP 3050 | 42 ± 5 | 0.98 ± 0.02 | 52± 5 | 33% | 5 | 85 / 15 | High Nitrile Rubber Content |
RA - 8020 | 40 ± 5 | 1.02 ± 0.02 | 50± 5 | 33% | 10 | 80 / 20 | Low PVC Content, Improved Compression Properties |
RA - 50 | 60 ± 5 | 1.11 ± 0.02 | 60± 5 | 33% | 12 | 50 / 50 | 50/50 Blend for High Ozone Resistance |
RA - S | 45 ± 5 | 1.09 ± 0.02 | 30± 5 | 33% | 20 | 30 / 20 | Polyblend for Soft, Low Hardness Products |
RA - SS | 30 ± 5 | 1.05 ± 0.02 | 25± 5 | 33% | 70 | 60/40/70 | Very Low Hardness Compound |
RA - 2530 | 50 ± 5 | 1.07 ± 0.02 | 50± 5 | 33% | 43 | 10/10/15 | Oil Extended and Low Hardness Applications |
RA - FRLT | 60 ± 5 | 1.08 ± 0.02 | 55± 5 | 33% | 9 | 70 / 30 | For Fire Retardancy |
RA - 73 | 55 ± 5 | 1.05 ± 0.02 | 60± 5 | 33% | 10 | 70 / 30 | Low Cost General Purpose |